ASTM D3552-96(2007)

This test method is designed to produce tensile property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the tensile response and should be reported include the following: material, methods of material preparation and lay-up, specimen stacking sequence, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, and volume percent reinforcement. Properties, in the test direction, which may be obtained from this test method include the following:

5.1.1 Ultimate tensile strength,

5.1.2 Ultimate tensile strain,

5.1.3 Tensile modulus of elasticity, and

5.1.4 Poissons ratio.

1.1 This test method covers the determination of the tensile properties of metal matrix composites reinforced by continuous and discontinuous high-modulus fibers. Nontraditional metal matrix composites as stated in also are covered in this test method. This test method applies to specimens loaded in a uniaxial manner tested in laboratory air at either room temperature or elevated temperatures. The types of metal matrix composites covered are:

1.1.1 Unidirectional - Any fiber-reinforced composite with all fibers aligned in a single direction. Continuous or discontinuous reinforcing fibers, longitudinal and transverse properties.

1.1.2 0/90 Balanced Crossply - A laminate composed of only 0 and 90 plies. This is not necessarily symmetric, continuous, or discontinuous reinforcing fibers.

1.1.3 Angleply Laminate - Any balanced laminate consisting of theta plies where theta is an acute angle with respect to a reference direction. Continuous reinforcing fibers without 0 reinforcing fibers (that is, (±45)ns, (±30)ns, and so forth).

1.1.4 Quasi-Isotropic Laminate - A balanced and symmetric laminate for which a constitutive property of interest, at a given point, displays isotropic behavior in the plane of the laminate. Continuous reinforcing fibers with 0 reinforcing fibers (that is, (0/±45/90)s, (0/±30)s, and so forth).

1.1.5 Unoriented and Random Discontinuous Fibers

1.1.6 Directionally Solidified Eutectic Composites

1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are provided for information purposes only.

This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.