1.1 This specification covers aluminum
and aluminum-alloy extruded bars, rods, wire, profiles, and tubes
in the aluminum alloys (Note 1) and tempers shown in Table 2.
Note
1—Throughout this specification, the use of the term alloy in the general sense includes aluminum as
well as aluminum alloy.
Note 2—For
rolled or cold-finished bar and rod refer to Specification B211,
for drawn seamless tube used in pressure applications,
Specification B210, for structural pipe and tube, Specification
B429/B429M, and for seamless pipe and tube used in pressure
applications, Specification B241/B241M.
Note
3—Structural pipe and tube produced in accordance with B221 is not
intended for fluid-carrying applications involving pressure. Refer
to either Specification B210 or B241/B241M, as appropriate, for
seamless pipe and tube used in fluid-carrying applications
involving pressure.
1.2 Alloy and temper designations are in
accordance with ANSI H35.1/H35.1M. The equivalent Unified Numbering
System alloy designations are those of Table 1 preceded by A9; for
example, A91100 for Aluminum 1100 in accordance with Practice
E527.
1.3 For acceptance criteria for inclusion
of new aluminum and aluminum alloys in this specification, see
Annex A2.
1.4 A complete metric companion to B221
has been developedB221M; therefore, no metric equivalents are
presented in this specification.
TABLE 1 Chemical Composition Limits
A,B,C
Note—In
case of a discrepancy between the values listed in Table 2 and
those listed in the “International
Alloy Designations and Chemical Composition Limits for Wrought
Aluminum and Wrought Aluminum Alloys”
(known as the “Teal Sheets”), the composition limits registered with the
Aluminum Association and published in the “Teal Sheets” should
be considered the controlling composition. The “Teal Sheets” are
available at http://www.aluminum.org/tealsheets.
|
Alloy |
Silicon |
Iron |
Copper |
Manga-
nese |
Magne-
sium |
Chromium |
Zinc |
Titanium |
Vanadium |
Other
ElementsD |
Aluminum |
| Each |
TotalE |
|
1060
|
0.25
|
0.35
|
0.05
|
0.03
|
0.03
|
...
|
0.05
|
0.03
|
0.05
|
0.03
|
...
|
99.60 minF
|
|
1100
|
0.95 Si + Fe
|
0.05–0.20
|
0.05
|
...
|
...
|
0.10
|
...
|
...
|
0.05G
|
0.15
|
99.00 minF
|
|
2014
|
0.50–1.2
|
0.7
|
3.9–5.0
|
0.40–1.2
|
0.20–0.8
|
0.10
|
0.25
|
0.15H
|
...
|
0.05H
|
0.15
|
remainder
|
|
2024
|
0.50
|
0.50
|
3.8–4.9
|
0.30–0.9
|
1.2–1.8
|
0.10
|
0.25
|
0.15H
|
...
|
0.05H
|
0.15
|
remainder
|
|
2219
|
0.20
|
0.30
|
5.8–6.8
|
0.20–0.40
|
0.02
|
...
|
0.10
|
0.02–0.10
|
0.05–0.15
|
0.05I
|
0.15I
|
remainder
|
|
3003
|
0.6
|
0.7
|
0.05–0.20
|
1.0–1.5
|
...
|
...
|
0.10
|
...
|
...
|
0.05
|
0.15
|
remainder
|
|
Alclad 3003
|
...
|
3003 Clad with 7072 alloy
|
...
|
...
|
...
|
...
|
...
|
...
|
...
|
...
|
|
3004
|
0.30
|
0.7
|
0.25
|
1.0–1.5
|
0.8–1.3
|
...
|
0.25
|
...
|
...
|
0.05
|
0.15
|
remainder
|
|
3102
|
0.40
|
0.7
|
0.10
|
0.05–0.40
|
...
|
...
|
0.30
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
5052
|
0.25
|
0.40
|
0.10
|
0.10
|
2.2–2.8
|
0.15–0.35
|
0.10
|
...
|
...
|
0.05
|
0.15
|
remainder
|
|
5083
|
0.40
|
0.40
|
0.10
|
0.40–1.0
|
4.0–4.9
|
0.05–0.25
|
0.25
|
0.15
|
...
|
0.05
|
0.15
|
remainder
|
|
5086
|
0.40
|
0.50
|
0.10
|
0.20–0.7
|
3.5–4.5
|
0.05–0.25
|
0.25
|
0.15
|
...
|
0.05
|
0.15
|
remainder
|
|
5154
|
0.25
|
0.40
|
0.10
|
0.10
|
3.1–3.9
|
0.15–0.35
|
0.20
|
0.20
|
...
|
0.05G
|
0.15
|
remainder
|
|
5454
|
0.25
|
0.40
|
0.10
|
0.50–1.0
|
2.4–3.0
|
0.05–0.20
|
0.25
|
0.20
|
...
|
0.05
|
0.15
|
remainder
|
|
5456
|
0.25
|
0.40
|
0.10
|
0.50–1.0
|
4.7–5.5
|
0.05–0.20
|
0.25
|
0.20
|
...
|
0.05
|
0.15
|
remainder
|
|
6005
|
0.6–0.9
|
0.35
|
0.10
|
0.10
|
0.40–0.6
|
0.10
|
0.10
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
6005A
|
0.50–0.9
|
0.35
|
0.30
|
0.50J
|
0.40–0.7
|
0.30J
|
0.20
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
6020K
|
0.40-0.9
|
0.50
|
0.30-0.9
|
0.35
|
0.6-1.2
|
0.15
|
0.20
|
0.15
|
…
|
0.05
|
0.15
|
remainder
|
|
6041L
|
0.50-0.9
|
0.15-0.7
|
0.15-0.6
|
0.05-0.20
|
0.8-1.2
|
0.05-0.15
|
0.25
|
0.15
|
…
|
0.05
|
0.15
|
remainder
|
|
6042M
|
0.50-1.2
|
0.7
|
0.20-0.6
|
0.40
|
0.7-1.2
|
0.04-0.35
|
0.25
|
0.15
|
…
|
0.05
|
0.15
|
remainder
|
|
6060
|
0.30–0.6
|
0.10–0.30
|
0.10
|
0.10
|
0.35–0.6
|
0.5
|
0.15
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
6061N
|
0.40–0.8
|
0.7
|
0.15–0.40
|
0.15
|
0.8–1.2
|
0.04–0.35
|
0.25
|
0.15
|
...
|
0.05
|
0.15
|
remainder
|
|
6063
|
0.20–0.6
|
0.35
|
0.10
|
0.10
|
0.45–0.9
|
0.10
|
0.10
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
6064O
|
0.40-0.8
|
0.7
|
0.15-0.40
|
0.15
|
0.8-1.2
|
0.05-0.14
|
0.25
|
0.15
|
…
|
0.05
|
0.15
|
remainder
|
|
6066
|
0.9–1.8
|
0.50
|
0.7–1.2
|
0.6–1.1
|
0.8–1.4
|
0.40
|
0.25
|
0.20
|
...
|
0.05
|
0.15
|
remainder
|
|
6070
|
1.0–1.7
|
0.50
|
0.15–0.40
|
0.40–1.0
|
0.50–1.2
|
0.10
|
0.25
|
0.15
|
...
|
0.05
|
0.15
|
remainder
|
|
6082
|
0.7–1.3
|
0.50
|
0.10
|
0.40–1.0
|
0.6–1.2
|
0.25
|
0.20
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
6105
|
0.6–1.0
|
0.35
|
0.10
|
0.15
|
0.45–0.8
|
0.10
|
0.10
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
6162
|
0.40–0.8
|
0.50
|
0.20
|
0.10
|
0.7–1.1
|
0.10
|
0.25
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
6262
|
0.40–0.8
|
0.7
|
0.15–0.40
|
0.15
|
0.8–1.2
|
0.04–0.14
|
0.25
|
0.15
|
...
|
0.05P
|
0.15P
|
remainder
|
|
6351
|
0.7–1.3
|
0.50
|
0.10
|
0.40–0.8
|
0.40–0.8
|
...
|
0.20
|
0.20
|
...
|
0.05
|
0.15
|
remainder
|
|
6360
|
0.35-0.8
|
0.10-0.30
|
0.15
|
0.02-0.15
|
0.25-0.45
|
0.05
|
0.10
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
6463
|
0.20–0.6
|
0.15
|
0.20
|
0.05
|
0.45–0.9
|
...
|
0.05
|
...
|
...
|
0.05
|
0.15
|
remainder
|
|
6560
|
0.30–0.7
|
0.10–0.30
|
0.05–0.20
|
0.20
|
0.20–0.6
|
0.05
|
0.15
|
0.10
|
...
|
0.05
|
0.15
|
remainder
|
|
7005
|
0.35
|
0.40
|
0.10
|
0.20–0.7
|
1.0–1.8
|
0.06–0.20
|
4.0–5.0
|
0.01–0.06
|
...
|
0.05Q
|
0.15Q
|
remainder
|
|
7072R
|
0.7 Si + Fe
|
0.10
|
0.10
|
0.10
|
...
|
0.8–1.3
|
...
|
...
|
|
|
remainder
|
|
7075
|
0.40
|
0.50
|
1.2–2.0
|
0.30
|
2.1–2.9
|
0.18–0.28
|
5.1–6.1
|
0.20S
|
...
|
0.05S
|
0.15
|
remainder
|
|
7116
|
0.15
|
0.30
|
0.50–1.1
|
0.05
|
0.8–1.4
|
...
|
4.2–5.2
|
0.05
|
0.05
|
0.05T
|
0.15
|
remainder
|
|
7129
|
0.15
|
0.30
|
0.50–0.9
|
0.10
|
1.3–2.0
|
0.10
|
4.2–5.2
|
0.05
|
0.05
|
0.05T
|
0.15
|
remainder
|
|
7178
|
0.40
|
0.50
|
1.6–2.4
|
0.30
|
2.4–3.1
|
0.18–0.28
|
6.3–7.3
|
0.20
|
...
|
0.05
|
0.15
|
remainder
|
A
Limits are in weight percent maximum unless shown as a range, or
stated otherwise.
B
Analysis shall be made for the elements for which limits are shown
in this table.
C
For the purpose of determining conformance to these limits, an
observed value or a calculated value obtained from analysis shall
be rounded to the nearest unit in the last right-hand place of the
figures used in expressing the specified limit, in accordance with
the rounding-off method of Practice E29.
D
Others includes listed elements for
which no specific limit is shown as well as unlisted metallic
elements. The producer may analyze samples for trace elements not
specified in the specification. However, such analysis is not
required and may not cover all metallic Others elements. Should any analysis by the
producer or the purchaser establish that an Others element exceeds the limit of Each or that the aggregate of several Others elements exceeds the limit of Total, the material shall be considered
nonconforming.
E
Other ElementsTotal shall be the sum of
unspecified metallic elements 0.010 % or more, rounded to the
second decimal before determining the sum.
F
The aluminum content shall be calculated by subtracting from 100.00
% the sum of all metallic elements present in amounts of 0.010 % or
more each, rounded to the second decimal before determining the
sum.
G
Be 0.0003 max for welding electrode, welding rod, and filler
wire.
H
Upon agreement between the purchaser and the producer or supplier,
a Zr + Ti limit of 0.20 % max is permitted. Properties in
Specification (Table 2) are not based on the Zirconium and Titanium
algorithm.
I
Zirconium, 0.10–0.25 %. The total for
other elements does not include zirconium.
J
Manganese plus chromium shall total 0.12–0.50.
K
Lead 0.05 % max, Tin 0.9-1.5 %.
L
Bismuth 0.30-0.9 %, Tin 0.35-1.2 %.
M
Bismuth 0.20-0.8 % Lead 0.15-0.40 %.
N
In 1965 the requirements for 6062 were combined with those for 6061
by revising the minimum chromium from “0.15 %”
to“ 0.04 %.” This action cancelled alloy 6062.
O
Bismuth 0.50-0.7 %, Lead 0.20-0.40 %,
P
Bismuth and lead shall be 0.40–0.7 %
each.
Q
Zirconium 0.08–0.20 %. The total for
other elements does not include zirconium.
R
Composition of cladding alloy applied during the course of
manufacture. Samples from finished tube shall not be required to
conform to these limits.
S
Upon agreement between the purchaser and the producer or supplier,
a Zr + Ti limit of 0.25 % max is permitted. Properties in
Specification (Table 2) are not based on the Zirconium and Titanium
algorithm.
T
Gallium 0.03 % max.
TABLE 2 Mechanical Property
LimitsA,B
Note—Strength values shown in parentheses are for
information only.
|
| Temper |
|
|
Specified Section
or Wall
Thickness, in. |
Area,
in.2 |
Tensile
Strength,
ksi |
Yield
Strength
(0.2 % offset), ksi |
Elongation in
2 in. or 4 ×
Diameter,
min, %C |
|
|
|
|
min |
max |
min |
max |
|
|
Aluminum 1060D
|
|
O
|
|
|
all
|
|
all
|
8.5
|
14.0
|
2.5
|
. . .
|
25
|
|
H112
|
|
|
all
|
|
all
|
8.5
|
. . .
|
2.5
|
. . .
|
25
|
|
Aluminum 1100D
|
|
O
|
|
|
all
|
|
all
|
11.0
|
15.5
|
3.0
|
. . .
|
25
|
|
H112
|
|
|
all
|
|
all
|
11.0
|
. . .
|
3.0
|
. . .
|
25
|
|
Alloy 2014D
|
|
O
|
|
|
all
|
|
all
|
. . .
|
30.0
|
. . .
|
18.0
|
12
|
|
T4
|
|
|
|
|
|
|
|
|
|
|
|
T4510E
|
|
all
|
|
all
|
50.0
|
. . .
|
35.0
|
. . .
|
12
|
|
T4511E
|
|
|
|
|
|
|
|
|
|
|
T42F
|
|
|
all
|
|
all
|
50.0
|
. . .
|
29.0
|
. . .
|
12
|
|
T6
|
|
|
up through 0.499
|
|
all
|
60.0
|
. . .
|
53.0
|
. . .
|
7
|
|
T6510E
|
0.500–0.749
|
|
all
|
64.0
|
. . .
|
58.0
|
. . .
|
7
|
|
T6511E
|
|
|
up through 25
|
68.0
|
. . .
|
60.0
|
. . .
|
7
|
|
|
0.750 and over
|
over 25 through 32
|
68.0
|
. . .
|
58.0
|
. . .
|
6
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
up through 0.749
|
|
all
|
60.0
|
. . .
|
53.0
|
. . .
|
7
|
|
T62F
|
|
|
|
up through 25
|
60.0
|
. . .
|
53.0
|
. . .
|
7
|
|
|
|
0.750 and over
|
|
|
|
|
|
|
|
|
|
|
|
over 25 through 32
|
60.0
|
. . .
|
53.0
|
. . .
|
6
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 2024D
|
|
O
|
|
|
all
|
|
all
|
. . .
|
35.0
|
. . .
|
19.0
|
12
|
|
|
|
|
up through 0.249
|
|
all
|
57.0
|
. . .
|
42.0
|
. . .
|
12G
|
|
T3
|
|
0.250–0.749
|
|
all
|
60.0
|
. . .
|
44.0
|
. . .
|
12G
|
|
T3510E
|
0.750–1.499
|
|
all
|
65.0
|
. . .
|
46.0
|
. . .
|
10
|
|
T3511E
|
|
|
up through 25
|
70.0
|
. . .
|
52.0H
|
. . .
|
10
|
|
|
|
1.500 and over
|
over 25 through 32
|
68.0
|
. . .
|
48.0I
|
. . .
|
8
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
up through 0.749
|
|
all
|
57.0
|
. . .
|
38.0
|
. . .
|
12
|
|
|
|
0.750–1.499
|
|
all
|
57.0
|
. . .
|
38.0
|
. . .
|
10
|
|
T42F
|
|
1.500 and over
|
|
up through 25
|
57.0
|
. . .
|
38.0
|
. . .
|
10
|
|
|
|
|
|
over 25 through 32
|
57.0
|
. . .
|
38.0
|
. . .
|
8
|
|
|
|
|
|
|
|
|
|
|
|
|
|
T81
|
|
|
0.050–0.249
|
|
all
|
64.0
|
. . .
|
56.0
|
. . .
|
4
|
|
T8510E
|
|
0.250–1.499
|
|
all
|
66.0
|
. . .
|
58.0
|
. . .
|
5
|
|
T8511E
|
|
1.500 and over
|
|
up through 32
|
66.0
|
. . .
|
58.0
|
. . .
|
5
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 2219D
|
|
O
|
|
|
all
|
|
all
|
. . .
|
32.0
|
. . .
|
18.0
|
12
|
|
T31
|
|
|
|
|
|
|
|
|
|
|
|
T3510E
|
|
|
up through 0.499
|
|
up through 25
|
42.0
|
. . .
|
26.0
|
. . .
|
14
|
|
T3511E
|
|
0.500–2.999
|
|
up through 25
|
45.0
|
. . .
|
27.0
|
. . .
|
14
|
|
|
|
|
|
|
|
|
|
|
|
|
|
T62F
|
|
|
up through 0.999
|
|
up through 25
|
54.0
|
. . .
|
36.0
|
. . .
|
6
|
|
|
|
1.000 and over
|
|
up through 25
|
54.0
|
. . .
|
36.0
|
. . .
|
6
|
|
T81
|
|
|
|
|
|
|
|
|
|
|
|
T8510E
|
|
up through 2.999
|
|
up through 25
|
58.0
|
. . .
|
42.0
|
. . .
|
6
|
|
T8511E
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 3003D
|
|
O
|
|
|
all
|
|
all
|
14.0
|
19.0
|
5.0
|
. . .
|
25
|
|
H112
|
|
|
all
|
|
all
|
14.0
|
. . .
|
5.0
|
. . .
|
25
|
|
Alloy Alclad 3003D
|
|
O
|
|
|
all
|
|
all
|
13.0
|
18.0
|
4.5
|
. . .
|
25
|
|
H112
|
|
|
all
|
|
all
|
13.0
|
. . .
|
4.5J
|
. . .
|
25
|
|
Alloy 3004D
|
|
O
|
|
|
all
|
|
all
|
23.0
|
29.0
|
8.5
|
. . .
|
. . .
|
|
Alloy 3102
|
|
H112K
|
|
|
0.028–0.050
|
|
all
|
11.0
|
18.0
|
4.0
|
. . .
|
25
|
|
Alloy 5052
|
|
O
|
|
|
all
|
|
all
|
25.0
|
35.0
|
10.0
|
. . .
|
. . .
|
|
Alloy 5083D
|
|
O
|
|
|
up through 5.000L
|
|
up through 32
|
39.0
|
51.0
|
16.0
|
. . .
|
14
|
|
H111
|
|
|
up through 5.000L
|
|
up through 32
|
40.0
|
. . .
|
24.0
|
. . .
|
12
|
|
H112
|
|
|
up through 5.000L
|
|
up through 32
|
39.0
|
. . .
|
16.0
|
. . .
|
12
|
|
Alloy 5086D
|
|
O
|
|
|
up through 5.000L
|
|
up through 32
|
35.0
|
46.0
|
14.0
|
. . .
|
14
|
|
H111
|
|
|
up through 5.000L
|
|
up through 32
|
36.0
|
. . .
|
21.0
|
. . .
|
12
|
|
H112
|
|
|
up through 5.000L
|
|
up through 32
|
35.0
|
. . .
|
14.0
|
. . .
|
12
|
|
Alloy 5154
|
|
O
|
|
|
all
|
|
all
|
30.0
|
41.0
|
11.0
|
. . .
|
. . .
|
|
H112
|
|
|
all
|
|
all
|
30.0
|
. . .
|
11.0
|
. . .
|
. . .
|
|
Alloy 5454D
|
|
O
|
|
|
up through 5.000L
|
|
up through 32
|
31.0
|
41.0
|
12.0
|
. . .
|
14
|
|
H111
|
|
|
up through 5.000L
|
|
up through 32
|
33.0
|
. . .
|
19.0
|
. . .
|
12
|
|
H112
|
|
|
up through 5.000L
|
|
up through 32
|
31.0
|
. . .
|
12.0
|
. . .
|
12
|
|
Alloy 5456D
|
|
O
|
|
|
up through 5.000L
|
|
up through 32
|
41.0
|
53.0
|
19.0
|
. . .
|
14
|
|
H111
|
|
|
up through 5.000L
|
|
up through 32
|
42.0
|
. . .
|
26.0
|
. . .
|
12
|
|
H112
|
|
|
up through 5.000L
|
|
up through 32
|
41.0
|
. . .
|
19.0
|
. . .
|
12
|
|
Alloy 6005
|
|
T1
|
|
|
up through 0.500
|
|
all
|
25.0
|
. . .
|
15.0
|
. . .
|
16
|
|
T5
|
|
|
up through 0.124
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
8
|
|
|
0.125–1.000
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 6005A
|
|
T1
|
|
|
up through 0.249
|
|
all
|
25.0
|
. . .
|
14.5
|
. . .
|
15
|
|
T5
|
|
|
up through 0.249
|
|
all
|
38.0
|
. . .
|
31.0
|
. . .
|
7
|
|
|
|
|
0.250–0.999
|
|
all
|
38.0
|
. . .
|
31.0
|
. . .
|
9
|
|
T61
|
|
|
up through 0.249
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
8
|
|
|
|
|
0.250–0.999
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
Alloy 6020
|
|
T6511
|
|
|
3.250-6.000
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
Alloy 6041
|
|
T6M
|
|
|
0.400-2.000
|
|
all
|
45.0
|
. . .
|
40.0
|
. . .
|
10
|
|
T6511M
|
|
|
0.400-2.000
|
|
all
|
45.0
|
. . .
|
40.0
|
. . .
|
10
|
|
Alloy 6042
|
|
T5
|
|
|
0.400-0.499
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
|
|
|
0.500-1.800
|
|
all
|
42.0
|
. . .
|
35.0
|
. . .
|
10
|
|
T5511
|
|
|
0.400-0.499
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
|
|
|
0.500-1.800
|
|
all
|
42.0
|
. . .
|
35.0
|
. . .
|
10
|
|
Alloy 6060
|
|
T51
|
|
|
up through 0.125
|
|
all
|
22.0
|
. . .
|
16.0
|
. . .
|
8
|
|
T61
|
|
|
up through 0.124
0.125–1.000
|
|
|
30.0
30.0
|
...
...
|
25.0
25.0
|
...
...
|
8
10
|
|
Alloy 6061D
|
|
O
|
|
|
all
|
|
all
|
. . .
|
22.0
|
. . .
|
16.0
|
16
|
|
T1
|
|
|
up through 0.625
|
|
all
|
26.0
|
. . .
|
14.0
|
. . .
|
16
|
|
T4
|
|
|
|
|
|
|
|
|
|
|
|
T4510E
|
|
all
|
|
all
|
26.0
|
. . .
|
16.0
|
. . .
|
16
|
|
T4511E
|
|
|
|
|
|
|
|
|
|
|
T42F
|
|
|
all
|
|
all
|
26.0
|
. . .
|
12.0
|
. . .
|
16
|
|
T51
|
|
|
up through 0.625
|
|
all
|
35.0
|
. . .
|
30.0
|
. . .
|
8
|
|
T6, T62F
|
|
|
|
|
|
|
|
|
|
|
|
T6510E
|
|
up through 0.249
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
8
|
|
T6511E
|
|
0.250 and over
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 6063
|
|
O
|
|
|
all
|
|
all
|
. . .
|
19.0
|
. . .
|
. . .
|
18
|
|
T1
|
|
|
up through 0.500
|
|
all
|
17.0
|
. . .
|
9.0
|
. . .
|
12
|
|
|
|
0.501–1.000
|
|
all
|
16.0
|
. . .
|
8.0
|
. . .
|
12
|
|
|
|
|
|
|
|
|
|
|
|
|
|
T4, T42F
|
|
|
up through 0.500
|
|
all
|
19.0
|
. . .
|
10.0
|
. . .
|
14
|
|
|
|
0.501–1.000
|
|
all
|
18.0
|
. . .
|
9.0
|
. . .
|
14
|
|
|
|
|
|
|
|
|
|
|
|
|
|
T5
|
|
|
up through 0.500
|
|
all
|
22.0
|
. . .
|
16.0
|
. . .
|
8
|
|
|
|
0.501–1.000
|
|
all
|
21.0
|
. . .
|
15.0
|
. . .
|
8
|
|
|
|
|
|
|
|
|
|
|
|
|
|
T52
|
|
|
up through 1.000
|
|
all
|
22.0
|
30.0
|
16.0
|
25.0
|
8
|
|
T54
|
|
|
up through 0.124
|
|
all
|
33.0
|
...
|
30.0
|
...
|
8
|
|
|
|
0.125–0.499
|
|
all
|
33.0
|
...
|
30.0
|
...
|
10
|
|
T6, T62F
|
|
|
up through 0.124
|
|
all
|
30.0
|
. . .
|
25.0
|
. . .
|
8
|
|
|
|
0.125–1.000
|
|
all
|
30.0
|
. . .
|
25.0
|
. . .
|
10
|
|
T65
|
|
|
up through 0.182
|
|
all
|
36.0
|
. . .
|
33.0
|
. . .
|
8
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 6064
|
|
T6M
|
|
|
0.400-2.000
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
T6511M
|
|
|
0.400-2.000
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
Alloy 6066
|
|
O
|
|
|
all
|
|
all
|
|
29.0
|
. . .
|
18.0
|
16
|
|
T4, T4510, T4511E
|
|
|
all
|
|
all
|
40.0
|
. . .
|
25.0
|
. . .
|
14
|
|
T42F
|
|
|
all
|
|
all
|
40.0
|
. . .
|
24.0
|
. . .
|
14
|
|
T6, T6510, T6511E
|
|
|
all
|
|
all
|
50.0
|
. . .
|
45.0
|
. . .
|
8
|
|
T62F
|
|
|
all
|
|
all
|
50.0
|
. . .
|
42.0
|
. . .
|
8
|
|
Alloy 6070
|
|
T6, T62
|
|
|
up through 2.999
|
|
up through 32
|
48.0
|
. . .
|
45.0
|
. . .
|
6
|
|
Alloy 6082
|
|
T6,T6511
|
|
|
0.200–0.750
|
|
all
|
45.0
|
...
|
38.0
|
...
|
6
|
|
|
|
0.751–6.000
|
|
all
|
45.0
|
....
|
38.0
|
....
|
8
|
|
|
|
6.001–8.000
|
|
all
|
41.0
|
...
|
35.0
|
...
|
6
|
|
Alloy 6105
|
|
T1
|
|
|
up through 0.500
|
|
all
|
25.0
|
. . .
|
15.0
|
. . .
|
16
|
|
T5
|
|
|
up through 0.124
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
8
|
|
|
|
0.125–1.000
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 6162
|
|
T5, T5510,E T5511E
|
|
|
up thru 1.000
|
|
all
|
37.0
|
. . .
|
34.0
|
. . .
|
7
|
|
T6, T6510,E T6511E
|
|
|
up thru 0.249
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
8
|
|
|
|
|
0.250–0.499
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
Alloy 6262
|
|
T6
|
|
|
|
|
|
|
|
|
|
|
|
T6510E
T6511E
|
|
all
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 6351
|
|
T1
|
|
|
up through 0.499
|
|
up through 20
|
26.0
|
. . .
|
13.0
|
. . .
|
15
|
|
T11
|
|
|
up through 0.749
|
|
all
|
26.0
|
. . .
|
16.0
|
. . .
|
16
|
|
T4
|
|
|
up through 0.749
|
|
all
|
32.0
|
. . .
|
19.0
|
. . .
|
16
|
|
T5
|
|
|
up through 0.249
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
8
|
|
|
|
|
0.250–1.000
|
|
all
|
38.0
|
. . .
|
35.0
|
. . .
|
10
|
|
T51
|
|
|
0.125–1.000
|
|
all
|
36.0
|
. . .
|
33.0
|
. . .
|
10
|
|
T54
|
|
|
up through 0.500
|
|
all
|
30.0
|
. . .
|
20.0
|
. . .
|
10
|
|
|
|
|
up through 0.124
|
|
all
|
42.0
|
. . .
|
37.0
|
. . .
|
8
|
|
T6
|
|
0.125–0.749
|
|
all
|
42.0
|
. . .
|
37.0
|
. . .
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 6360
|
|
T5
|
|
|
up through 0.250
|
|
all
|
22.0
|
. . .
|
16.0
|
. . .
|
8
|
|
T6
|
|
|
up through 0.120
|
|
all
|
30.0
|
. . .
|
25.0
|
. . .
|
8
|
|
|
|
|
0.121–0.250
|
|
all
|
30.0
|
. . .
|
25.0
|
. . .
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 6463
|
|
T1
|
|
|
up through 0.500
|
|
up through 20
|
17.0
|
. . .
|
9.0
|
. . .
|
12
|
|
T5
|
|
|
up through 0.500
|
|
up through 20
|
22.0
|
. . .
|
16.0
|
. . .
|
8
|
|
T6
|
|
|
up through 0.124
|
|
up through 20
|
30.0
|
. . .
|
25.0
|
. . .
|
8
|
|
|
|
0.125–0.500
|
|
up through 20
|
30.0
|
. . .
|
25.0
|
. . .
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 6560
|
|
T5
|
|
|
0.090–0.125
|
|
all
|
22.0
|
...
|
16.0
|
...
|
8
|
|
T6
|
|
|
0.090–0.125
|
|
all
|
30.0
|
...
|
25.0
|
...
|
8
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 7005
|
|
T53
|
|
|
up through 0.750
|
|
all
|
50.0
|
. . .
|
44.0
|
. . .
|
10
|
|
Alloy 7075D
|
|
O
|
|
|
all
|
|
all
|
. . .
|
40.0
|
. . .
|
24.0
|
10
|
|
|
|
|
up through 0.249
|
|
all
|
78.0
|
. . .
|
70.0
|
. . .
|
7
|
|
|
|
0.250–0.499
|
|
all
|
81.0
|
. . .
|
73.0
|
. . .
|
7
|
|
T6, T62F
|
|
0.500–1.499
|
|
all
|
81.0
|
. . .
|
72.0
|
. . .
|
7
|
|
T6510E
|
1.500–2.999
|
|
all
|
81.0
|
. . .
|
72.0
|
. . .
|
7
|
|
T6511E
|
3.000–4.499
|
|
up through 20
|
81.0
|
. . .
|
71.0
|
. . .
|
7
|
|
|
|
|
over 20 through 32
|
78.0
|
. . .
|
70.0
|
. . .
|
6
|
|
|
|
4.500–5.000
|
|
up through 32
|
78.0
|
. . .
|
68.0
|
. . .
|
6
|
|
|
|
|
|
|
|
|
|
|
|
|
|
T73
|
|
|
0.062–0.249
|
|
up through 20
|
68.0
|
. . .
|
58.0
|
. . .
|
7
|
|
T73510E
|
0.250–1.499
|
|
up through 25
|
70.0
|
. . .
|
61.0
|
. . .
|
8
|
|
T73511E
|
1.500–2.999
|
|
up through 25
|
69.0
|
. . .
|
59.0
|
. . .
|
8
|
|
|
|
3.000–4.499
|
|
up through 20
|
68.0
|
. . .
|
57.0
|
. . .
|
7
|
|
|
|
|
|
|
over 20 through 32
|
65.0
|
. . .
|
55.0
|
. . .
|
7
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
up through 0.049
|
|
all
|
73.0
|
. . .
|
63.0
|
. . .
|
7
|
|
T76
|
|
0.050–0.124
|
|
all
|
74.0
|
. . .
|
64.0
|
. . .
|
7
|
|
T76510E
|
0.125–0.249
|
|
up through 20
|
74.0
|
. . .
|
64.0
|
. . .
|
7
|
|
T76511E
|
0.250–0.499
|
|
up through 20
|
75.0
|
. . .
|
65.0
|
. . .
|
7
|
|
|
|
0.500–1.000
|
|
up through 20
|
75.0
|
. . .
|
65.0
|
. . .
|
7
|
|
|
|
1.001–2.000
|
|
up through 20
|
75.0
|
. . .
|
65.0
|
. . .
|
7
|
|
|
|
2.001–3.000
|
|
up through 20
|
74.0
|
. . .
|
64.0
|
. . .
|
7
|
|
|
|
3.001–4.000
|
|
up through 20
|
74.0
|
. . .
|
63.0
|
. . .
|
7
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Alloy 7116
|
|
T5
|
|
|
0.125–0.500
|
|
all
|
48.0
|
. . .
|
42.0
|
. . .
|
8
|
|
Alloy 7129
|
|
T5, T6
|
|
|
up through 0.500
|
|
all
|
55.0
|
. . .
|
49.0
|
. . .
|
9
|
|
Alloy 7178D
|
|
O
|
|
|
all
|
|
up through 32
|
. . .
|
40.0
|
. . .
|
24.0
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
up through 0.061
|
|
up through 20
|
82.0
|
. . .
|
76.0
|
. . .
|
. . .
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0.062–0.249
|
|
up through 20
|
84.0
|
. . .
|
76.0
|
. . .
|
5
|
|
T6
|
|
0.250–1.499
|
|
up through 25
|
87.0
|
. . .
|
78.0
|
. . .
|
5
|
|
T6510E
|
1.500–2.499
|
|
up through 25
|
86.0
|
. . .
|
77.0
|
. . .
|
5
|
|
T6511E
|
over 25 through 32
|
84.0
|
. . .
|
75.0
|
. . .
|
5
|
|
|
|
2.500–2.999
|
|
up through 32
|
82.0
|
. . .
|
71.0
|
. . .
|
5
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
up through 0.061
|
|
up through 20
|
79.0
|
. . .
|
73.0
|
. . .
|
5
|
|
|
|
0.062–0.249
|
|
up through 20
|
82.0
|
. . .
|
74.0
|
. . .
|
5
|
|
|
|
0.250–1.499
|
|
up through 25
|
86.0
|
. . .
|
77.0
|
. . .
|
5
|
|
T62F
|
|
|
|
|
|
|
|
|
|
|
|
|
1.500–2.499
|
|
up through 25
|
86.0
|
. . .
|
77.0
|
. . .
|
5
|
|
|
|
|
over 25 through 32
|
84.0
|
. . .
|
75.0
|
. . .
|
5
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
2.500–2.999
|
|
up through 32
|
82.0
|
. . .
|
71.0
|
. . .
|
5
|
|
|
|
|
|
|
|
|
|
|
|
|
|
T76
|
|
|
0.125–0.249
|
|
up through 20
|
76.0
|
. . .
|
66.0
|
. . .
|
7
|
|
T76510E
|
0.250–0.499
|
|
up through 20
|
77.0
|
. . .
|
67.0
|
. . .
|
7
|
|
T76511E
|
0.500–1.000
|
|
up through 20
|
77.0
|
. . .
|
67.0
|
. . .
|
7
|
A
The basis for establishment of tensile property limits is shown in
Annex A1.
B
To determine conformance to this specification, each value shall be
rounded to the nearest 0.1 ksi for strength and nearest 0.5 % for
elongation in accordance with the rounding-off-method of Practice
E29.
C
Elongation of full-section and cut-out sheet-type specimens is
measured in 2 in. Elongation of cut-out round specimens is measured
in 4× specimen diameter. See 8.1.1 and
8.1.2 for conditions under which measurements are not required.
D
These alloys are also produced in the F temper for which no tensile
properties are specified or guaranteed.
E
For stress relieved tempers (T3510, T3511, T4510, T4511, T5510,
T5511, T6510, T6511, T73510, T73511, T76510, T76511, T8510, T8511),
characteristics and properties other than those specified may
differ somewhat from the corresponding characteristics and
properties of material in the basic tempers.
F
Material in the T42 and T62 tempers is not available from the
material producers.
G
Minimum elongation for tube, 10 %.
H
Minimum yield strength for tube, 48.0 ksi.
I
Minimum yield strength for tube, 46.0 ksi.
J
Yield strength is not applicable in tube.
K
Only in tube form.
L
Properties not applicable to extruded tube over 2.999 in wall
thickness.
M
Tentative; properties subject to revision.
|