Standard Test Method for Evaluation of Transparent Plastics Exposed to Accelerated Weathering Combined with Biaxial Stress (Includes all amendments And changes 12/17/2014).
Automaticky přeložený název:
Standardní zkušební metoda pro hodnocení průhledných plastů na místech vystavených Urychlené stárnutí kombinaci s biaxiálním Stres
NORMA vydána dne 15.5.2009
Označení normy: ASTM F1164-97(2009)e1
Poznámka: NEPLATNÁ
Datum vydání normy: 15.5.2009
Kód zboží: NS-49358
Počet stran: 4
Přibližná hmotnost: 12 g (0.03 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Keywords:
accelerated weathering, biaxial stress, coating adhesion, crazing, transparent plastics, Aerospace transparent enclosures, Composite plastic materials/applications, Conditioning, Crazing--aerospace plastics, Degradation--plastics, Fresnel-reflector system, Haze, Light transmission and reflection, Pressure testing--aerospace materials, Resistance--aircraft/aerospace materials, Stress--aerospace materials, Visual examination--aerospace applications, Weathering (aerospace materials/applications)
Significance and Use | ||||||||||
The degradation of optical properties of transparent plastics is the single greatest cause for in-service removal and replacement. Some optical qualities are inherent in the geometry, manufacturing process, and materials, and remain relatively unchanged after manufacture, while others are subject to gradual change during exposure to the service environment. Factors having an influence on the crazing of transparent plastics include stress, ultraviolet (UV), moisture, and temperature. Sufficient data has been generated to make it evident that real-world conditioning must be experienced by developmental test specimens, as opposed to testing new unexposed material to determine durability, prior to in-service usage. However, the laboratory simulation of natural weathering, and especially accelerated simulation, is imprecise and correlation of results obtained for different plastics or from using different exposure apparatus should not be attempted until a valid database has been generated for such cross-correlation. |
||||||||||
1. Scope | ||||||||||
1.1 This test method covers the resistance of transparent plastics exposed to environmental conditioning (accelerated weathering) under a biaxial stress state induced by a pressure cell/test fixture. 1.2 The values stated in acceptable metric units are to be regarded as the standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||
2. Referenced Documents | ||||||||||
|
Chcete pravidelně odebírat informace o nově vycházejících normách z celého světa a to zcela zdarma?
Přihlašte se k odběru. Vše je velice jednoduché a absolutně ZDARMA.
Na výběr máte vydavatele z celého světa.
Poslední aktualizace: 04.11.2024 (Počet položek: 2 209 323)
© Copyright 2024 NORMSERVIS s.r.o.