Standard Test Method for Indentation Softening Temperature by Thermomechanical Analysis
Automaticky přeložený název:
Standardní zkušební metoda pro odsazení teplota měknutí termomechanickým analýzy
NORMA vydána dne 1.4.2011
Označení normy: ASTM E2347-11
Poznámka: NEPLATNÁ
Datum vydání normy: 1.4.2011
Kód zboží: NS-45092
Počet stran: 5
Přibližná hmotnost: 15 g (0.03 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Keywords:
penetration temperature, softening, strain, stress, temperature, thermomechanical analysis (TMA), vicat temperature, ICS Number Code 83.080.01 (Plastics in general)
1. Scope | ||||||||||||
1.1 This test method is applicable to materials that soften upon heating to a modulus less than 6.0 MPa. This test method describes the determination of the temperature at which the specific modulus of either 6.65 (Method A) or 33.3 MPa (Method B) (equivalent to Test Method D 1525) of a test specimen is realized by indentation measurement using a thermomechanical analyzer as the test specimen is heated. This temperature is identified as the indentation softening temperature. The test may be performed over the temperature range of ambient to 300C. Note 1—This test method is intended to provide results similar to those of Test Method D 1525 but is performed on a thermomechanical analyzer using a smaller diameter indenting probe. Equivalence of results to those obtained by Test Method D 1525 has been demonstrated on a limited number of materials. Until the user demonstrates equivalence, the results of this Test Method shall be considered to be independent and unrelated to those of Test Method D 1525. 1.2 This test method is not recommended for ethyl cellulose, poly (vinyl chloride), poly (vinylidene chloride) and other materials having a large measurement imprecision (see Test Method D 1525 and sections and ). 1.3 Electronic instrumentation or automated data analysis and reduction systems or treatments equivalent to this test method may be used. Note 2—Since all electronic data treatments are not equivalent, the user shall verify equivalency to this test method. 1.4 SI values are the standard. 1.5 There is no ISO standard equivalent to this test method. 1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||||
2. Referenced Documents | ||||||||||||
|
Historická
1.4.2013
Historická
1.4.2011
Historická
1.11.2013
Historická
1.4.2010
Historická
15.3.2011
Historická
1.6.2013
Poslední aktualizace: 21.11.2024 (Počet položek: 2 206 478)
© Copyright 2024 NORMSERVIS s.r.o.