Standard Practice for Extreme Value Analysis of Nonmetallic Inclusions in Steel and Other Microstructural Features
Automaticky přeložený název:
Standardní praxe pro extrémní hodnoty Analýza nekovových inkluzí v oceli a dalších mikrostrukturních funkce
NORMA vydána dne 1.2.2008
Označení normy: ASTM E2283-08
Poznámka: NEPLATNÁ
Datum vydání normy: 1.2.2008
Kód zboží: NS-44912
Počet stran: 11
Přibližná hmotnost: 33 g (0.07 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Keywords:
extreme value statistics, inclusion length, maximum inclusion length, maximum likelihood method, Extreme value statistics, Inclusion length, Inclusions, Indigenous inclusions, Maximum inclusion length, Metallographic analysis/inspection, Microstructures, Nonmetallic inclusions, Statistical methods--metals/alloys, Steel, Value analysis (VA), ICS Number Code 77.040.99 (Other methods of testing metals)
Significance and Use | ||||||||||||||||||
This practice is used to assess the indigenous inclusions or second-phase constituents in metals using extreme value statistics. It is well known that failures of mechanical components, such as gears and bearings, are often caused by the presence of large nonmetallic oxide inclusions. Failure of a component can often be traced to the presence of a large inclusion. Predictions related to component fatigue life are not possible with the evaluations provided by standards such as Test Methods E 45, Practice E 1122, or Practice E 1245. The use of extreme value statistics has been related to component life and inclusion size distributions by several different investigators (3-8). The purpose of this practice is to create a standardized method of performing this analysis. This practice is not suitable for assessing the exogenous inclusions in steels and other metals because of the unpredictable nature of the distribution of exogenous inclusions. Other methods involving complete inspection such as ultrasonics must be used to locate their presence. |
||||||||||||||||||
1. Scope | ||||||||||||||||||
1.1 This practice describes a methodology to statistically characterize the distribution of the largest indigenous nonmetallic inclusions in steel specimens based upon quantitative metallographic measurements. The practice is not suitable for assessing exogenous inclusions. 1.2 Based upon the statistical analysis, the nonmetallic content of different lots of steels can be compared. 1.3 This practice deals only with the recommended test methods and nothing in it should be construed as defining or establishing limits of acceptability. 1.4 The measured values are stated in SI units. For measurements obtained from light microscopy, linear feature parameters shall be reported as micrometers, and feature areas shall be reported as micrometers. 1.5 The methodology can be extended to other materials and to other microstructural features. 1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||||||||||
2. Referenced Documents | ||||||||||||||||||
|
Chcete mít jistotu, že používáte pouze platné technické normy?
Nabízíme Vám řešení, které Vám zajistí měsíční přehled o aktuálnosti norem, které používáte.
Chcete vědět více informací? Podívejte se na tuto stránku.
Poslední aktualizace: 01.11.2024 (Počet položek: 2 208 817)
© Copyright 2024 NORMSERVIS s.r.o.