Standard Test Method for Optical Emission Vacuum Spectrometric Analysis of Stainless Steel by the Point-to-Plane Excitation Technique
Automaticky přeložený název:
Standardní zkušební metoda pro Optická emisní vakuové spektrometrickou analýzu z nerezové oceli , které Point -to - Plane Budící Technika
NORMA vydána dne 1.10.2008
Označení normy: ASTM E1086-08
Poznámka: NEPLATNÁ
Datum vydání normy: 1.10.2008
Kód zboží: NS-40387
Počet stran: 5
Přibližná hmotnost: 15 g (0.03 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Keywords:
atomic emission, point-to-plane technique, spectrometric analysis, stainless steel, Carbon content--metals/alloys, Chemical analysis--metals/alloys, Chromium content--metals/alloys, Copper content--metals/alloys, Manganese content--metals/alloys, Molybdenum content--metals/alloys, Nickel content--metals/alloys, Phosphorus content--metals/alloys, Silicon content--metals/alloys, Spectrochemical analysis--steel, Sulfur--metals/alloys, Optical emission vacuum spectrometric analysis
Significance and Use | ||||||||||||||||||||
The chemical composition of stainless steels must be determined accurately in order to ensure the desired metallurgical properties. This procedure is suitable for manufacturing control and inspection testing. |
||||||||||||||||||||
1. Scope | ||||||||||||||||||||
1.1 This test method covers for the
atomic emission vacuum spectrometric analysis of stainless steel in
solid form by the point-to-plane excitation technique for the
following elements in the concentration ranges shown:
1.2 This test method is designed for the routine analysis of chill-cast disks or inspection testing of stainless steel samples that have a flat surface of at least 13 mm (0.5 in.) in diameter. The samples must be sufficiently massive to prevent overheating during the discharge and of a similar metallurgical condition and composition as the reference materials. 1.3 Analytical curves are plotted using the concentration ratio method as shown in Practice E 158. One or more of the reference materials must closely approximate the composition of the specimen. The technique of analyzing reference materials along with unknowns and performing the indicated mathematical corrections may also be used to correct for interference effects and to compensate for errors resulting from instrument drift. A variety of such systems are commonly used. Any of these that will achieve analytical accuracy equivalent to that reported for this test method are acceptable. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||||||||||||
2. Referenced Documents | ||||||||||||||||||||
|
Chcete mít jistotu, že používáte pouze platné technické normy?
Nabízíme Vám řešení, které Vám zajistí měsíční přehled o aktuálnosti norem, které používáte.
Chcete vědět více informací? Podívejte se na tuto stránku.
Poslední aktualizace: 08.09.2024 (Počet položek: 2 346 102)
© Copyright 2024 NORMSERVIS s.r.o.