ASTM E101-91
Test Method for Spectrographic Analysis of Aluminum and Aluminum Alloys by the Point-To-Plane Technique (Withdrawn 1996)
Automaticky přeložený název:
Zkušební metoda pro spektrografickou Analýza hliníku a hliníkových slitin technikou point-to - Plane (Withdrawn 1996 )
NORMA vydána dne 1.1.1991
Informace o normě:
Označení normy: ASTM E101-91
Poznámka: NEPLATNÁ
Datum vydání normy: 1.1.1991
Kód zboží: NS-40124
Počet stran: 5
Přibližná hmotnost: 15 g (0.03 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Anotace textu normy ASTM E101-91 :
Keywords:
Aluminum-spectrochemical analysis, Aluminum alloys-spectrochemical analysis, Aluminum content-Al/Al alloys, Bismuth content-Al/Al alloys, Calcium content-Al/Al alloys, Chromium content-Al/Al alloys, Copper content-Al/Al alloys, Iron content-Al/Al alloys, Magnesium content-Al/Al alloys, Manganese content-Al/Al alloys, Nickel content-Al/Al alloys, Silicon content-Al/Al alloys, Sodium content-aluminum/aluminum alloys, Spectrographic analysis, Tin content-Al/Al alloys, Titanium content-Al/Al alloys
Doplňující informace
| 1. Scope |
|
1.1 This test method covers the spectrographic analysis of aluminum and aluminum alloys for the following elements in the ranges indicated: Element Concentration Range, % Silicon 0.02 to 14.0 Copper 0.001 to 10.0 Magnesium 0.001 to 10.0 Zinc 0.03 to 8.0 Nickel 0.03 to 3.0 Iron 0.02 to 2.0 Manganese 0.005 to 2.0 Lead 0.03 to 0.7 Bismuth 0.03 to 0.7 Chromium 0.01 to 0.5 Titanium 0.01 to 0.5 Tin 0.01 to 0.5 Beryllium 0.0002 to 0.5 Calcium 0.0005 to 0.1 Sodium 0.0005 to 0.051.2 This test method is applicable primarily to the analysis of chill-cast disks, but it may be extended, with proper precautions, to the analysis of samples in other forms on which a flat surface for sparking can be machined. Standards and samples should be of similar composition and metallurgical state; when they are not, corrections must be applied to compensate for these effects. 1.3 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
Doporučujeme:
Aktualizace technických norem
Chcete mít jistotu, že používáte pouze platné technické normy?
Nabízíme Vám řešení, které Vám zajistí měsíční přehled o aktuálnosti norem, které používáte.
Chcete vědět více informací? Podívejte se na tuto stránku.