Standard Test Method of Measuring Shrinkage from Mold Dimensions of Thermoplastics
Automaticky přeložený název:
Standardní zkušební metoda měření smrštění od Mold Rozměry termoplastů
NORMA vydána dne 1.11.2008
Označení normy: ASTM D955-08
Poznámka: NEPLATNÁ
Datum vydání normy: 1.11.2008
Kód zboží: NS-39889
Počet stran: 5
Přibližná hmotnost: 15 g (0.03 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Keywords:
mold shrinkage, shrinkage, thermoplastics, Molding/extrusion compounds/materials, Mold shrinkage, Shrinkage--plastics, Thermosetting plastics, ICS Number Code 83.140.10 (Films and sheets)
Significance and Use | ||||||||||||||||||||||||
Injection Molding—In injection molding, the difference between the dimensions of a mold cavity and of the molded specimen may vary according to the design of the mold and operation of the molding process. Factors such as mold and melt temperature, fill times, and packing conditions are known to affect shrinkage significantly. Adherence to the specified mold design (see 7.1) and specifications outlined in Practice D 3641 or ISO 294-4 or the appropriate material specification will improve the reproducibility of the test. Compression Molding—In compression molding, the difference between the dimensions of a mold cavity and of the molded specimen may vary according to the design of the mold and operation of the molding process. Factors, such as the amount of material in charge, cooling time, and pressure application are known to affect shrinkage significantly. Adherence to the specified mold design (see 7.2) and specifications outlined in Practice D 4703 or ISO 293 or the appropriate material specifications will improve the reproducibility of the test. |
||||||||||||||||||||||||
1. Scope | ||||||||||||||||||||||||
1.1 This test method is intended to measure shrinkage from mold cavity to molded dimensions of thermoplastics when molded by compression or injection processes with specified process conditions. 1.2 This test method covers shrinkage measurements at 24 and 48 h. 1.3 This method will give comparable data based on standard specimens and can not predict absolute values in actual molded parts with varying flow paths, wall thicknesses, pressure and temperature gradients and process conditions. Differences in mold shrinkage may also be observed among the three specimen geometries described in this test method. 1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are given for information only. 1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Note 1—This standard and ISO 294-3 are equivalent in the design of specimen D2. This test method is equivalent to ISO 294-4 where Type D2 specimens and the procedure in Appendix X2 are used. |
||||||||||||||||||||||||
2. Referenced Documents | ||||||||||||||||||||||||
|
Chcete pravidelně odebírat informace o nově vycházejících normách z celého světa a to zcela zdarma?
Přihlašte se k odběru. Vše je velice jednoduché a absolutně ZDARMA.
Na výběr máte vydavatele z celého světa.
Poslední aktualizace: 12.09.2024 (Počet položek: 2 346 316)
© Copyright 2024 NORMSERVIS s.r.o.