Standard Test Methods for Nonrigid Vinyl Chloride Polymer Tubing Used for Electrical Insulation
Automaticky přeložený název:
Standardní zkušební metody pro Nonrigid vinylchloridu Polymer hadiček používaných pro elektrickou izolaci
NORMA vydána dne 1.10.2009
Označení normy: ASTM D876-09
Poznámka: NEPLATNÁ
Datum vydání normy: 1.10.2009
Kód zboží: NS-39568
Počet stran: 13
Přibližná hmotnost: 39 g (0.09 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Keywords:
brittleness temperature, corrosion, dielectric breakdown voltage, dimensions, electrical insulation, flammability, oil resistance, penetration, poly(vinyl chloride), PVC, temperature tests, tension properties/tests, tubing, vinyl chloride polymer, volume resistivity, Breakdown voltage, Brittleness temperature, Corrosivity, Dielectric breakdown voltage, Electrical insulating materials, Electrical insulating plastics, Electrical resistance/resistivity--insulating materials
Significance and Use | |||||||||||||||||||||||||||||||||||||||||||||
These test methods include most of the test methods that are considered important to characterize nonrigid vinyl chloride polymer tubing. While they were developed initially for this type of extruded tubing, their use is not limited to this type of tubing. Variations in these test methods or alternate contemporary methods may be used to determine the values for the properties in this standard provided such methods ensure quality levels and measurement accuracy equal to or better than those prescribed herein. It is the responsibility of the organizations using alternate test methods to be able to demonstrate this condition. In cases of dispute, the test methods specified herein shall be used. Note 2—Provision for alternate methods is necessary because of (1) the desire to simplify procedures for specific applications without altering the result, and (2) the desire to eliminate redundant testing and use data generated during manufacturing process control, including that generated under Statistical Process Control (SPC) conditions, using equipment and methods other than those specified herein. An example would be the use of laser micrometers or optical comparators to measure dimensions. |
|||||||||||||||||||||||||||||||||||||||||||||
1. Scope | |||||||||||||||||||||||||||||||||||||||||||||
1.1 These test methods cover the testing of general-purpose (Grade A), low-temperature (Grade B), and high-temperature (Grade C) nonrigid vinyl chloride polymer tubing, or its copolymers with other materials, for use as electrical insulation. For the purpose of these test methods nonrigid tubing shall be tubing having an initial elongation in excess of 100 % at break. Note 1—These test methods are similar but not identical to those in IEC 60684–2. 1.2 The values stated in inch-pound units are to be regarded as standard, except for temperature, which shall be expressed in degrees Celsius. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 The procedures appear in the following sections:
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements, see Section 5. 1.5 For fire test caveats, see Section 15. 15.1 This is a fire-test-response standard. The test procedure described measures the resistance of the tubing to ignition or the spread of flame after ignition when tested under the specified conditions. 15.2 This standard is used to measure and describe the response of materials, products, or assemblies to heat and flame under controlled conditions, but does not by itself incorporate all factors required for fire hazard or fire risk assessment of the materials, products, or assemblies under actual fire conditions. 15.3 Fire testing is inherently hazardous. Adequate safeguards for personnel and property shall be employed in conducting these tests. 25.1 The effect of elevated temperature is indicated by the changes in ultimate elongation and weight caused by exposure of the tubing to elevated temperatures for a specified time under controlled conditions of air circulation. |
|||||||||||||||||||||||||||||||||||||||||||||
2. Referenced Documents | |||||||||||||||||||||||||||||||||||||||||||||
|
Chcete pravidelně odebírat informace o nově vycházejících normách z celého světa a to zcela zdarma?
Přihlašte se k odběru. Vše je velice jednoduché a absolutně ZDARMA.
Na výběr máte vydavatele z celého světa.
Poslední aktualizace: 16.09.2024 (Počet položek: 2 433 731)
© Copyright 2024 NORMSERVIS s.r.o.