Practice for Accelerated Aging of LeatherPřeložit název
NORMA vydána dne 1.1.2023
Označení normy: ASTM D8137-18(2023)
Datum vydání normy: 1.1.2023
Kód zboží: NS-1100836
Počet stran: 7
Přibližná hmotnost: 21 g (0.05 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
accelerated aging, acid gases, leather deterioration, longevity, tensile strength,, ICS Number Code 59.140.30 (Leather and furs)
|Significance and Use
6.1?A substantial difficulty in using leather in applications requiring very long service lives is estimating how well a particular leather will actually hold up in service. Such applications may include use in musical instruments such as pipe organs, bookbinding leathers, etc. Use of leather in pipe organs in the past (prior to approximately 1930) demonstrated service lives frequently over 100 years, and the consequences of short service lives can result in extremely costly repairs. Many post-1930 leathers have had short service lives (as little as 15 years) due to the use of various more modern tannages and processing methods. Identifying exactly what tannage and processing was used in a particular leather and how successful this tanning and processing was can be very difficult. Failure of bookbinding and upholstery leathers formed the impetus for extensive work by leather chemists in the 1940s to identify tests that could be used to verify the durability of leather samples. Early studies by Cheshire and Frey & Beebe1.1?This practice is based on studies relating the rate of deterioration of leathers having known durabilities from long-term storage of samples, to the deterioration experienced by laboratory exposure of specimens to known contents of acid gases in air or oxygen. This is accomplished by measuring the deterioration (reduction in tensile strength) of leather specimens when they are subjected to exposure to a mixture of air, moisture and sulfur dioxide at a given temperature and pressure and for a given exposure time. The loss of tensile strength of the specimens resulting from this exposure is compared to that experienced by a variety of leathers having various tannages and having historically long and short service lifetimes. The initial tensile strength and the degree of loss of tensile strength is related to what service life can be anticipated from a given leather.
1.2?This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.3?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Chcete pravidelně odebírat informace o nově vycházejících normách z celého světa a to zcela zdarma?
Přihlašte se k odběru. Vše je velice jednoduché a absolutně ZDARMA.
Na výběr máte vydavatele z celého světa.
Poslední aktualizace: 23.02.2024 (Počet položek: 2 880 529)
© Copyright 2024 NORMSERVIS s.r.o.