ASTM D7005/D7005M-15
Standard Test Method for Determining the Bond Strength (Ply Adhesion) of Geocomposites This test method is under the jurisdiction of ASTM Committee D35 on Geosynthetics and is the direct responsibility of Subcommittee D35.01 on Mechanical Properties. Current edition approved July 1, 2015. Published July 2015. Originally approved in 2003. Last previous edition approved in 2008 as -03(2008). DOI: 10.1520/D7005_D7005M-15.
Automaticky přeložený název:
Standardní zkušební metodu pro stanovení Soudržnost ( Ply adheze) z geokompozita Tato zkušební metoda je pod jurisdikci ASTM výboru D35 na Geosynthetics a jepřímou odpovědnost podvýboru D35.01 na mechanické vlastnosti. Aktuální vydání schválen 1. července 2015. publikována v červenci 2015. Původně schválený v roce 2003. Poslední předchozím vydání schválen v roce 2008 jako -03 (2008). DOI: 10,1520 / D7005_D7005M -15.
NORMA vydána dne 1.7.2015
Informace o normě:
Označení normy: ASTM D7005/D7005M-15
Poznámka: NEPLATNÁ
Datum vydání normy: 1.7.2015
Kód zboží: NS-611371
Počet stran: 4
Přibližná hmotnost: 12 g (0.03 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Kategorie - podobné normy:
Anotace textu normy ASTM D7005/D7005M-15 :
Keywords:
bond strength, geocomposite, laminates, ply adhesion strength,, ICS Number Code 59.080.70 (Geotextiles)
Doplňující informace
| Significance and Use | ||||||||||||||
|
5.1 This test method is to be used as a quality control or quality assurance test. As a manufacturing quality control (MQC) test, it would generally be used by the geocomposite product manufacturer or fabricator. As a construction quality assurance (CQA) test, it would be used by certification or inspection organizations. 5.2 This test method can also be used to verify if the adhesion or bond strength varies after exposure to various incubation media in durability or chemical resistance testing, or both. 5.3 Whatever use is to be associated with the test, it should be understood that this is an index test. Note 2: There have been numerous attempts to relate the
results of this test to the interface shearing resistance of the
respective materials determined per Test Method D5321/D5321M. To date, no relationships
have been established between the two properties.
5.4 Test Method D7005/D7005M for determining the bond strength (ply adhesion) strength may be used as an acceptance test of commercial shipments of geocomposites, but caution is advised since information about between-laboratory precision is incomplete. Comparative tests as directed in 5.4.1 are advisable. 5.4.1 In the case of a dispute arising from differences in reported test results when using the procedure in Test Method D7005/D7005M for acceptance of commercial shipments, the purchaser and the supplier should first confirm that the tests were conducted using comparable test parameters including specimen conditioning, grip faces, grip size, etc. Comparative tests should then be conducted to determine if there is a statistical bias between their laboratories. Competent statistical assistance is recommended for the investigation of bias. As a minimum, the two parties should take a group of test specimens that are as homogeneous as possible and that are from a lot of the material in question. The test specimens should be randomly assigned to each laboratory for testing. The average results from the two laboratories should be compared to the Student's t-test for unpaired data and an acceptable probability level chosen by the two parties before the testing is begun. If a bias is found, either its cause must be found and corrected or the purchaser and supplier must agree to interpret future test results in the light of the known bias. Refer to Practice D2905, Table 1. |
||||||||||||||
| 1. Scope | ||||||||||||||
|
1.1 It has been widely discussed in the literature that bond strength of flexible multi-ply materials is difficult to measure with current technology. The above is recognized and accepted, since all known methods of measurement include the force required to bend the separated layers, in addition to that required to separate them. However, useful information can be obtained when one realizes that the bending force is included and that direct comparison between different materials, or even between the same materials of different thickness, cannot be made. Also, conditioning that affects the moduli of the plies will be reflected in the bond strength measurement. 1.2 This index test method defines a procedure for comparing the bond strength or ply adhesion of geocomposites. The focus is on geotextiles bonded to geonets or other types of drainage cores; for example, geomats, geospacers, etc. Other possible uses are geotextiles adhered or bonded to themselves, geomembranes, geogrids, or other dissimilar materials. Various processes can make such laminates: adhesives, thermal bonding, stitch bonding, needling, spread coating, etc. 1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in 11.1.1. |
||||||||||||||
| 2. Referenced Documents | ||||||||||||||
|
Odebírejte informace o nově vydaných normách ZDARMA:
Chcete pravidelně odebírat informace o nově vycházejících normách z celého světa a to zcela zdarma?
Přihlašte se k odběru. Vše je velice jednoduché a absolutně ZDARMA.
Na výběr máte vydavatele z celého světa.