Standard Test Method for Measurements of Internal Stresses in Organic Coatings by Cantilever (Beam) Method
Přeložit název
NORMA vydána dne 1.6.2022
Označení normy: ASTM D6991-17(2022)
Datum vydání normy: 1.6.2022
Kód zboží: NS-1066069
Počet stran: 5
Přibližná hmotnost: 15 g (0.03 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Keywords:
cantilever, deflection, internal stress, organic coatings,, ICS Number Code 25.220.60 (Organic coatings)
Significance and Use | ||||||
5.1Stresses in coatings arise as a result of their shrinkage or expansion if expected movements are prevented by coating adhesion to its substrate. 5.2There are several causes leading to arrival of stresses in the coatings: film formation (cross-linking, solvent evaporation, etc.); differences in thermal expansion coefficients between coating and substrate; humidity and water absorption; environmental effects (ultraviolet radiation, temperature and humidity), and others. 5.3Knowledge of the internal stresses in coatings is very important because they may effect coating performance and service life. If the internal stress exceeds the tensile strength of the film, cracks are formed. If stress exceeds adhesion between coating and substrate, it will reduce adhesion and can lead to delamination of coatings. Quantitative information about stresses in coatings can be useful in coating formulation and recommendations for their application and use. 5.4This method has been found useful for air-dry industrial organic coatings but the applicability has not yet been assessed for thin coatings (thickness <0.0254 mm (.001 in.), for powder and thermally-cured coatings. |
||||||
1. Scope | ||||||
1.1This test method covers the procedure for measurements of internal stresses in organic coatings by using the cantilever (beam) method. 1.2This method is appropriate for the coatings for which the modulus of elasticity of substrate (Es) is significantly greater than the modulus of elasticity of coating (Ec) and for which the thickness of substrate is significantly greater than thickness of coating (see Note 7 and Note 8). 1.3The stress values are limited by the adhesion values of coating to the substrate and by the tensile strength of the coating, or both. 1.4The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. 1.5This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and to determine the applicability of regulatory limitations prior to use. 1.6This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||
2. Referenced Documents | ||||||
|