Standard Test Method for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials by Four-Point Bending (Includes all amendments and changes 7/14/2020).
Přeložit název
NORMA vydána dne 1.3.2017
Označení normy: ASTM D6272-17e1
Datum vydání normy: 1.3.2017
Kód zboží: NS-999989
Počet stran: 9
Přibližná hmotnost: 27 g (0.06 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Keywords:
flexural properties, four point bending, plastics, stiffness, strength,, ICS Number Code 29.035.20 (Plastic and rubber insulating materials), 83.080.01 (Plastics in general)
Significance and Use | ||||||||||||||||||||
5.1 Flexural properties determined by this test method are especially useful for quality control and specification purposes. 5.2 This test method is recommended for those materials that do not fail within the strain limits imposed by Test Method D790. The major difference between four point and three point bending modes is the location of the maximum bending moment and maximum axial fiber stress. In four point bending the maximum axial fiber stress is uniformly distributed between the loading noses. In three point bending the maximum axial fiber stress is located immediately under the loading nose. 5.3 Flexural properties vary with specimen depth, temperature, atmospheric conditions, and the difference in rate of straining specified in Procedures A and B. 5.4 Before proceeding with this test method, reference the specification of the material being tested. Any test specimen preparation, conditioning, dimensions, or testing parameters covered in the material specification, or both, shall take precedence over those mentioned in this test method. If there are no material specifications, then these default conditions apply. Table 1 in Classification D4000 lists the ASTM materials standards that currently exist. |
||||||||||||||||||||
1. Scope | ||||||||||||||||||||
1.1 This test method covers the determination of flexural properties of unreinforced and reinforced plastics, including high-modulus composites and electrical insulating materials in the form of rectangular bars molded directly or cut from sheets, plates, or molded shapes. These test methods are generally applicable to rigid and semirigid materials. However, flexural strength cannot be determined for those materials that do not break or that do not fail in the outer fibers. This test method utilizes a four point loading system applied to a simply supported beam. 1.2 This test method describes two procedures (Procedure A and Procedure B), the selection of which depends on the behavior of the sample to be tested as explained below: 1.2.1 Procedure A, designed principally for materials that break at comparatively small deflections. It shall be used for measurement of flexural properties, particularly flexural modulus, unless the material specification states otherwise. 1.2.2 Procedure B, designed particularly for those materials that undergo large deflections during testing. It is suitable for measurement of flexural strength. 1.3 Comparative tests are permitted to be run according to either procedure, provided that the procedure is found satisfactory for the material being tested. 1.4 The values stated in SI units are to be regarded as the standard. The values provided in parentheses are for information only. 1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Note 1: This test method is similar to ISO 14125, Method B.
However, ISO 14125, Method B specifies only a load span of
1/3 the support span whereas D6272 also
permits a load span of 1/2 the support
span. For this reason and other differences in technical content,
exercise extreme care if attempting to compare results between the
two test methods.
|
||||||||||||||||||||
2. Referenced Documents | ||||||||||||||||||||
|
Chcete pravidelně odebírat informace o nově vycházejících normách z celého světa a to zcela zdarma?
Přihlašte se k odběru. Vše je velice jednoduché a absolutně ZDARMA.
Na výběr máte vydavatele z celého světa.
Poslední aktualizace: 03.11.2024 (Počet položek: 2 209 203)
© Copyright 2024 NORMSERVIS s.r.o.