ASTM D2584-18

4.1 This test method is used to obtain the ignition loss of a cured reinforced resin sample.

4.2 If only glass fabric or filament is used as the reinforcement of an organic resin that is completely decomposed to volatile materials under the conditions of this test and the small amount of volatiles (water, residual solvent) that are potentially present are ignored, the ignition loss shall be considered to be the resin content of the sample.

1.1 This test method covers the determination of the ignition loss of cured reinforced resins. This ignition loss shall be considered to be the resin content within the limitations of 4.2.

1.2 The values stated in SI units are to be regarded as the standard.

1.3 This standard is used to measure and describe the response of composite material to heat under controlled conditions, but does not by itself incorporate all of the factors required for fire hazard or fire assessments of the composite materials under actual fire conditions.

1.4 Fire testing is inherently hazardous. Adequate safeguards for personnel and property shall be employed in conducting these tests.

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.