This specification covers clay roof tiles with such durability and appearance that can provide a weather-resistant surface of a specified design. Each tile should be manufactured from clay, shale, or similar naturally occurring earthy substances and subjected to high-temperature firing. The heat treatment should develop a fired bond between material particles that provides the required strength and durability. The tiles should be shaped by molding, pressing, or extrusion during manufacture. Generally, the tiles are planar or undulating rectangular and are classified into three grades according to the degree of resistance to weathering. Materials are also grouped into three types according to profile and rise-to-width ratio. Colors and textures produced by application of inorganic coatings are allowed except when the coloring is done by flashing or the texturing by sanding where the sand does not form a continuous coating. Each tile should conform to the specified values of durability, freezing and thawing, transverse breaking strength, efflorescence, reactive particulates, and permeability.
Keywords:
absorption, clay, clay roof tile, durability, freeze thaw durability, permeability, roof, roofing, tile, transverse breaking strength,, ICS Number Code 91.100.25 (Terracotta building products)
Doplňující informace
| 1. Scope | ||||||||
|
1.1?This specification covers clay tiles intended for use as roof covering where durability and appearance are required to provide a weather-resistant surface of specified design. 1.2?Tiles are manufactured from clay, shale, or similar naturally occurring earthy substances and subjected to heat treatment at elevated temperatures (firing). The heat treatment must develop a fired bond between the particulate constituents to provide the strength and durability requirements of this specification (see firing and fired bond in Terminology C1232). 1.3?Tiles are shaped during manufacture by molding, pressing, or extrusion and it is permitted to use the shaping method to describe the tiles. 1.4?Tiles are generally planar or undulating rectangular shapes available in a variety of cross-sectional profiles, shapes, sizes, surface textures, and colors. 1.5?Three grades of tile having various degrees of resistance to weathering are covered in this specification. Three types of tile are defined to cover the features that influence appearance. 1.6?The text of this specification references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard. 1.7?The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.8?This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.9?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||