ASTM B848/B848M-21
Standard Specification for Powder Forged (PF) Ferrous Materials
Přeložit název
NORMA vydána dne 1.9.2021
Informace o normě:
Označení normy: ASTM B848/B848M-21
Datum vydání normy: 1.9.2021
Kód zboží: NS-1035613
Počet stran: 10
Přibližná hmotnost: 30 g (0.07 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Kategorie - podobné normy:
Anotace textu normy ASTM B848/B848M-21 :
This specification covers the powder forged ferrous materials fabricated by hot densification of atomized prealloyed or iron powders and intended for use as structural parts. The strcutural parts shall be made by hot forging of powder metallurgy preforms in confined dies with or without subsequent heat treatment. The materials shall conform to the required chemical composition for nickel, molybdenum, manganese, copper, chromium, sulfur, silicon, phosphorus, carbon, and oxygen. The mechanical properties such as yield strength, elongation, Rockwell hardness, impact energy, compressive yield strength and fatigue shal be determined using the tensile test method, Charpy V-notch impact energy test method, and hardness test method. The materials shall conform to the required surface finger oxide penetration, interparticle oxide networks, decarburization depth, and nonmetallic inclusion level.
Keywords:
powder forged (PF) parts, powder forged (PF) steels, powder forging (PF),, ICS Number Code 77.160 (Powder metallurgy)
Doplňující informace
| 1. Scope |
|
1.1?This specification covers powder forged ferrous materials fabricated by hot densification of atomized prealloyed or iron powders and intended for use as structural parts. 1.2?This specification covers powder forged parts made from the following materials: 1.2.1?Compositions:? 1.2.1.1?PF-10XX Carbon Steel (produced from atomized iron powder and graphite powder), 1.2.1.2?PF-10CXX Copper-Carbon Steel (produced from atomized iron powder, copper and graphite powders), 1.2.1.3?PF-11XX Carbon Steel with manganese sulfide for enhanced machinability (produced from atomized iron powder, manganese sulfide, and graphite powders), 1.2.1.4?PF-11CXX, PF-1130CXX, and PF-1135CXX Copper-Carbon Steels with manganese sulfide for enhanced machinability (produced from atomized iron powder, copper, manganese sulfide, and graphite powders), 1.2.1.5?PF-42XX Nickel-Molybdenum Steel (produced from prealloyed atomized iron-nickel-molybdenum powder and graphite powder), 1.2.1.6?PF-46XX Nickel-Molybdenum Steel (produced from prealloyed atomized iron-nickel-molybdenum powder and graphite powder), 1.2.1.7?PF-44XX Molybdenum Steel (produced from prealloyed atomized iron-molybdenum powder and graphite powder), and 1.2.1.8?PF-49XX Molybdenum Steel (produced from prealloyed atomized iron-molybdenum powder and graphite powder). Note 1:?Alloy composition designations are modifications of
the AISI-SAE nomenclature. For example: 10CXX designates a plain
carbon steel containing copper and XX amount of carbon.
Compositional limits of alloy and impurity elements may be
different from the AISI-SAE limits. Chemical composition limits are
specified in Section 6.
Note 2:?XX designates the forged carbon content, in hundredths
of a percent, that is specified by the purchaser for the
application. For a given specified carbon content, the permissible
limits shall be as specified in 6.2.
Note 3:?The old acronym for powder forging P/F has been
replaced by PF throughout the document. The change in the prefix
for the material designations is just to match the currently
approved acronym for powder forging. No change has been made to the
material specification and performance characteristics for the
various powder forged materials.
1.2.2?Grades:? 1.2.2.1?Grade ADensity equivalent to a maximum of 0.5 % porosity. The minimum density of those sections of the powder forged part so designated by the applicable part drawing shall not be less than the value specified in Table 1. 1.2.2.2?Grade BDensity equivalent to a maximum of 1.5 % porosity. The minimum density of those sections of the powder forged part so designated by the applicable part drawing shall not be less than the value specified in Table 1. 1.3?UnitsThe values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined. 1.4?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
Odebírejte informace o nově vydaných normách ZDARMA:
Chcete pravidelně odebírat informace o nově vycházejících normách z celého světa a to zcela zdarma?
Přihlašte se k odběru. Vše je velice jednoduché a absolutně ZDARMA.
Na výběr máte vydavatele z celého světa.