ASTM B247-20
Standard Specification for Aluminum and Aluminum-Alloy Die Forgings, Hand Forgings, and Rolled Ring Forgings
Přeložit název
NORMA vydána dne 1.5.2020
Informace o normě:
Označení normy: ASTM B247-20
Datum vydání normy: 1.5.2020
Kód zboží: NS-994945
Počet stran: 13
Přibližná hmotnost: 39 g (0.09 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Kategorie - podobné normy:
Anotace textu normy ASTM B247-20 :
This specification covers aluminum and aluminum-alloy die forgings, hand forgings, and rolled ring forgings and includes the following UNS alloy designations: A91100, A92014, A92018, A92025, A92219, A92618, A93003, A94032, A95083, A96061, A96066, A96151, A97049, A97050, A97075, A97076, and A97175. Tempers covered by this specification includes: H112, T4, T6, T61, T73, T74, T7352, T7452, T7454, T652, T852, and H111 as well as F and 01 types. The forgings may be manufactured by pressing, hammering, or rolling, at the option of the producer. Requirements for quality assurance, chemical analysis, tension and hardness tests, heat treatment, heat-treat response, and stress corrosion resistance and stress-corrosion cracking test are detailed. The forgings shall conform to the chemical composition requirements prescribed for aluminum, silicon, iron, copper, manganese, magnesium, chromium, nickel, zinc, zirconium, and titanium. Forgings having the specified thickness shall meet the requirements specified for the mechanical properties such as tensile strength, yield strength, elongation, and Brinell hardness.
Keywords:
aluminum alloy, die forgings, hand forgings, rolled ring forgings,, ICS Number Code 77.150.10 (Aluminium products)
Doplňující informace
| 1. Scope | ||||||||||||||||||||||||||||||||||||||||||||||||
|
1.1 This specification2 covers aluminum-alloy (Note 1) die forgings, hand forgings, and rolled ring forgings as shown in Table 2, Table 3, and Table 4 in Section 10 for heat-treatable alloy forgings supplied in the F and 01 tempers. The maximum thicknesses for forgings within the scope of this specification are as indicated in those tables. Note 1: Throughout this specification use of the term
Note 2: For forging stock supplied as rolled, cold-finished
bar, extruded bar, or rod see Specification B211/B211M.
1.2 Alloy and temper designations are in accordance with ANSI H35.1/H35.1(M). The equivalent Unified Numbering System alloy designations are those of Table 1 preceded by A9, for example, A91100 for aluminum 1100 in accordance with Practice E527. 1.3 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2. 1.4 This specification is the inch-pound companion to Specification B247M; therefore, no SI equivalents are presented in the specification. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||||||||||||||||||||||||||||||||||||||||
| 2. Referenced Documents | ||||||||||||||||||||||||||||||||||||||||||||||||
|
Odebírejte informace o nově vydaných normách ZDARMA:
Chcete pravidelně odebírat informace o nově vycházejících normách z celého světa a to zcela zdarma?
Přihlašte se k odběru. Vše je velice jednoduché a absolutně ZDARMA.
Na výběr máte vydavatele z celého světa.