Standard Specification for Forged Carbon and Alloy Steel Flanges for Low-Temperature Service
Přeložit název
NORMA vydána dne 1.11.2019
Označení normy: ASTM A707/A707M-19
Datum vydání normy: 1.11.2019
Kód zboží: NS-976069
Počet stran: 6
Přibližná hmotnost: 18 g (0.04 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
This specification covers forged carbon and alloy steel flanges intended primarily for petroleum and gas pipelines in areas subject to low ambient temperatures. Eight grades, four yield-strength classes, and three different notch toughness levels are included. All material shall be heat treated by annealing, normalizing, precipitation hardening, quenching-and-tempering, normalizing-and-tempering, normalizing-and-precipitation hardening, or quenching-and-precipitation hardening. A chemical heat analysis shall be made and conform to the requirements as to chemical composition specified. The material in the weld neck shall conform to the mechanical property requirements specified. Hardness test, impact test, ultrasonic test, tension test, and hydrostatic test shall be made to conform to the specified requirements.
Keywords:
carbon equivalent, piping applications, pressure containing parts, residual elements, steel flanges, steel forgings, alloy, steel forgings, carbon, temperature service applications, low,, ICS Number Code 23.040.60 (Flanges, couplings and joints)
1. Scope | ||||||||||||||||
1.1 This specification covers forged carbon and alloy steel flanges intended primarily for petroleum and gas pipelines in areas subject to low ambient temperatures. Included are flanges to specified dimensions or to dimensional standards such as those MSS, ASME, and API specifications that are referenced in Section 2. 1.2 Supplementary requirements are provided for use when additional requirements are desired. These shall apply only when specified individually by the purchaser in the order. 1.3 Eight grades, four yield-strength classes, and three different notch toughness levels are included. 1.4 The availability of a particular size of flange of a specific grade and class is limited only by the capability of the composition to meet the specified mechanical property requirements. However, current practice normally limits the following: (a) Grade L1 to Classes 1 and 2, (b) Grade L2 to Classes 1, 2, and 3, (c) Grade L3 to Classes 1, 2, and 3, (d) Grade L4 to Classes 1, 2, and 3, (e) Grade L7 to Classes 1 and 2, and (f) Grades L5, L6, and L8 are generally available in any class. 1.5 This specification is expressed in both inch-pound units and in SI units. However, unless the order specifies the applicable “M” specification designation (SI units), the material shall be furnished to inch-pound units. 1.6 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. 1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||||||||