Standard Test Methods for Chill Testing of Cast Iron
Přeložit název
NORMA vydána dne 1.1.2022
Označení normy: ASTM A367-22
Datum vydání normy: 1.1.2022
Kód zboží: NS-1046460
Počet stran: 4
Přibližná hmotnost: 12 g (0.03 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
This test method deals with gray irons that are to be free of chill in the casting and to chilled irons that are to have a specific depth of chill in the casting. The purpose of the test is to determine the chilling tendencies of cast iron. The two tests are wedge test and chill test. Both tests shall be made in a core which may either be single cores or gang cores and a pouring practice shall be performed. The wedge test is generally better adapted to the higher strength gray irons. The accelerated cooling rate that shall induce the formation of a chill shall be brought about through the design of the test specimen. The chill test is better adapted to the softer grades of gray iron and should be used if the casting have a specified depth of chill. The chill in this type of test shall be induced by casting one edge of the test specimen against a metal or graphite chilled plate or block. Wedge test is simpler than chill test since in the wedge test, maintenance of chill blocks or plates is not necessary.
Keywords:
ICS Number Code 77.140.80 (Iron and steel castings)
1. Scope | ||||||||||||||||||||||||||||||||||||||||||||||||
1.1?These test methods for chill testing apply to gray irons that are to be free of chill in the casting and to chilled irons that are to have a specific depth of chill in the casting. Two test methods for determining the chilling tendencies of cast iron are covered as follows. For many applications, either test method will be satisfactory if test pieces of the proper dimensions are selected. 1.1.1?Test Method A, Wedge TestThis test is adapted for the higher-strength gray irons. The accelerated cooling rate to induce the formation of a chill is brought about through the design of the test specimen. This test method is simpler than Test Method B since maintenance of chill blocks or plates is not necessary. 1.1.2?Test Method B, Chill TestThis test is adapted for the softer grades of gray iron and should be used if the casting is to have a specified depth of chill. The chill in this type of test is induced by casting one edge of the test specimen against a metal or graphite chilled plate or block. 1.2?The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered to be part of the standard. 1.2.1?The metric equivalency charts in Figs. 1 and 2 are provided for information only.
1.3?This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||||||||||||||||||||||||||||||||||||||||
Chcete mít jistotu, že používáte pouze platné technické normy?
Nabízíme Vám řešení, které Vám zajistí měsíční přehled o aktuálnosti norem, které používáte.
Chcete vědět více informací? Podívejte se na tuto stránku.
Poslední aktualizace: 29.07.2024 (Počet položek: 2 339 192)
© Copyright 2024 NORMSERVIS s.r.o.