Standard Specification for Liquid and Paste Fluxes for Soldering of Copper and Copper Alloy Tube
NORMA vydána dne 1.5.2016
Proč Redline?
Redline představuje rychlý a snadný způsob jak porovnat všechny změny mezi aktuální platnou normou a předchozí verzí.
Díky redline se okamžitě dozvíte o:
Ušetřete si čas i starosti!
Díky Redline již nebudete muset ztrácet čas zjišťováním, co se v nové normě změnilo. Redline Vám ušetří čas a zaručí, že se o změnách v normě dozvíte.
Cena
Pokud si zvolíte možnost "Platná norma + Redline", pak dostanete oba dokumenty! A co je nejlepší, cena Platné normy + Redline je pouze o něco málo vyšší než cena samostatné platné normy.
Designation standards: ASTM B813-16
Publication date standards: 1.5.2016
The number of pages: 7
Approximate weight : 21 g (0.05 lbs)
Country: American technical standard
Kategorie: Technické normy ASTM
This guide establishes the requirements and test methods for liquid and paste fluxes for joining by soldering of copper and copper alloy tube and fittings in plumbing, heating, air conditioning, mechanical, fire sprinkler, and other similar systems. There shall be a clear indication that in the areas of flux reaction, the sheets shall show a corrosion and residue-free surface comparable with the unwetted areas as determined by visual inspection. Samples of flux taken for the purpose of the tests listed in this specification shall be selected from the stock of the manufacturer and shall be representative of the material being evaluated. The specimen shall undergo the spreading test wherein the oven shall be equipped with a sight glass for visible control of the melting of the solder. The specimen shall then pass the aggressiveness test wherein the aggressiveness of the flux is determined by means of a resistivity test of an aqueous solution of the flux residue. The conductivity cell to be used shall be kept immersed in distilled water at ambient temperature for a given minimum number of hours before use. Resistivity tests shall be performed for both soldered and unsoldered specimen. The specimen shall then undergo corrosive test by being dipped onto ethanol.
Keywords:
aggressiveness test, copper and copper alloys, corrosiveness, flushing, liquid and paste fluxes, resistivity, soldering, spreading factor, tarnish, viscosity,, ICS Number Code 25.160.50 (Brazing and soldering)