Standard Specification for Aluminum-Alloy Permanent Mold Castings
NORMA vydána dne 1.9.2019
Proč Redline?
Redline představuje rychlý a snadný způsob jak porovnat všechny změny mezi aktuální platnou normou a předchozí verzí.
Díky redline se okamžitě dozvíte o:
Ušetřete si čas i starosti!
Díky Redline již nebudete muset ztrácet čas zjišťováním, co se v nové normě změnilo. Redline Vám ušetří čas a zaručí, že se o změnách v normě dozvíte.
Cena
Pokud si zvolíte možnost "Platná norma + Redline", pak dostanete oba dokumenty! A co je nejlepší, cena Platné normy + Redline je pouze o něco málo vyšší než cena samostatné platné normy.
Designation standards: ASTM B108/B108M-19
Publication date standards: 1.9.2019
The number of pages: 23
Approximate weight : 69 g (0.15 lbs)
Country: American technical standard
Kategorie: Technické normy ASTM
This specification covers aluminum-alloy permanent mold castings. The responsibility of furnishing castings that can be laid out and machined to the finished dimensions within the permissible variations specified shall rest with the producer, except where mold equipment is furnished by the purchaser. Samples for chemical analysis shall be taken by sawing, drilling, or milling the casting or test specimens in such a manner as to be representative of the material. Unless otherwise specified, only aluminum or producers foundry scrap shall be used in the re-melting furnace from which molten metal is taken for pouring directly into castings. Pure materials, recycled materials, and master alloys may be used to make alloys conforming to this specification. Foundry control shall consist of examination of castings by radiographic or other approved methods for determining internal discontinuities until the gating, pouring, and other foundry practices have been established to produce castings meeting the quality standards furnished by the purchaser or agreed upon by the purchaser and the producer. Separately cast test specimens shall be cast in iron molds. If the castings are to be heat treated and separately cast specimens are to be used, the specimens representing such castings shall be heat treated with the castings they represent. If castings are to be heat treated and tests are to be obtained on the castings, the test specimens shall be taken from the castings after heat treatment. One per melt-heat combination shall be tested when tensile properties of castings are to be determined. The finished castings shall be uniform in composition and free of blowholes, cracks, shrinks, and other discontinuities.
Keywords:
aluminum, permanent mold castings,, ICS Number Code 77.150.10 (Aluminium products)