Standard Test Method for Young´s Modulus, Tangent Modulus, and Chord Modulus
Přeložit název
NORMA vydána dne 15.7.2017
Informace o normě:
Označení normy: ASTM E111-17
Datum vydání normy: 15.7.2017
Kód zboží: NS-693818
Počet stran: 7
Přibližná hmotnost: 21 g (0.05 liber)
Země: Americká technická norma
Kategorie: Technické normy ASTM
Kategorie - podobné normy:
Anotace textu normy ASTM E111-17 :
Keywords:
chord modulus, stress-strain diagram, tangent modulus, Young´s modulus,, ICS Number Code 77.040.10 (Mechanical testing of metals)
Doplňující informace
| Significance and Use |
|
5.1 The value of Young’s modulus is a material property useful in design for calculating compliance of structural materials that follow Hooke's law when subjected to uniaxial loading (that is, the strain is proportional to the applied force). 5.2 For materials that follow nonlinear elastic stress-strain behavior, the value of tangent or chord modulus is useful in estimating the change in strain for a specified range in stress. 5.3 Since for many materials, Young's modulus in tension is different from Young's modulus in compression, it shall be derived from test data obtained in the stress mode of interest. 5.4 The accuracy and precision of apparatus, test specimens, and procedural steps should be such as to conform to the material being tested and to a reference standard, if available. 5.5 Precise determination of Young’s modulus requires due regard for the numerous variables that may affect such determinations. These include (1) characteristics of the specimen such as orientation of grains relative to the direction of the stress, grain size, residual stress, previous strain history, dimensions, and eccentricity; (2) testing conditions, such as alignment of the specimen, speed of testing, temperature, temperature variations, condition of test equipment, ratio of error in applied force to the range in force values, and ratio of error in extension measurement to the range in extension values used in the determination; and (3) interpretation of data (see Section 9). 5.6 When the modulus determination is made at strains in excess of 0.25 %, correction shall be made for changes in cross-sectional area and gauge length, by substituting the instantaneous cross section and instantaneous gauge length for the original values. 5.7 Compression results may be affected by barreling (see Test Methods E9). Strain measurements should therefore be made in the specimen region where such effects are minimal. |
| 1. Scope |
|
1.1 This test method covers the determination of Young's modulus, tangent modulus, and chord modulus of structural materials, see Fig. 1. This test method is limited to materials in which and to temperatures and stresses at which creep is negligible compared to the strain produced immediately upon loading and to elastic behavior. FIG. 1 Stress-Strain Diagrams Showing Straight Lines Corresponding to ( |
1.2 Because of experimental problems associated with the establishment of the origin of the stress-strain curve described in 8.1, the determination of the initial tangent modulus (that is, the slope of the stress-strain curve at the origin) and the secant modulus are outside the scope of this test method.
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
|
Standard Test Methods of Compression Testing of Metallic Materials at Room Temperature |
|
|
Method for Static Determination of Young's Modulus of Metals at Low and Elevated Temperatures (Withdrawn 1985) |
|
|
Standard Terminology Relating to Methods of Mechanical Testing (Includes all amendments and changes 3/29/2023). |
|
|
Standard Practices for Force Calibration and Verification of Testing Machines |
|
|
Standard Test Methods for Tension Testing of Metallic Materials |
|
|
Standard Practice for Verification and Classification of Extensometer Systems |
|
|
Standard Practice for Verification of Testing Frame and Specimen Alignment Under Tensile and Compressive Axial Force Application |
|
|
Standard Test Methods for Elevated Temperature Tension Tests of Metallic Materials |